Synthesis of high aspect ratio titanate nanotubes


Reference:

Torrente-Murciano, L., Lapkin, A. A. and Chadwick, D., 2010. Synthesis of high aspect ratio titanate nanotubes. Journal of Materials Chemistry, 20 (31), pp. 6484-6489.

Related documents:

This repository does not currently have the full-text of this item.
You may be able to access a copy if URLs are provided below. (Contact Author)

Official URL:

http://dx.doi.org/10.1039/c0jm01212b

Abstract

Titanate nanotubes were synthesised using a hydrothermal method in a static and a rotating autoclave (end-over-end) over a range of rotation speeds (0-20 rpm). The control of the average length of the titanate nanotubes by the speed of rotation during their synthesis was revealed. As the rotation speed was increased, longer nanotubes (more than 1 mm at 20 rpm) were produced. This phenomenon was attributed to an increase in the mass transfer, facilitating the formation of longer intermediate titanate nanosheets. Long nanotubes self-assemble, forming secondary structures without transformation into nanowires as confirmed by the high specific surface area, pore size (inner nanotubes diameter) of 3.7 nm, XRD and Raman analyses. The initial phase of dissolution of the ends of the nanotubes was observed at higher rotation speeds. Pre-sonication treatment of the suspension of TiO(2) precursor in NaOH solution resulted in a slight increase in the length of the nanotubes in the static synthesis, but did not have any effect in the rotating autoclave syntheses.

Details

Item Type Articles
CreatorsTorrente-Murciano, L., Lapkin, A. A. and Chadwick, D.
DOI10.1039/c0jm01212b
DepartmentsFaculty of Engineering & Design > Chemical Engineering
RefereedYes
StatusPublished
ID Code25525

Export

Actions (login required)

View Item